SPARTAN HAZEL

SPARTAN HAZELPropiedad Descripcin Valor Composicin Composition Superficie Surface: 100% Vinilo Vinyl Soporte Backing: 100% Polister Polyester Peso Weight 800 g m Ancho Width 140 cm 2 % Grosor Thickness 1,3 mm Resistencia a la abrasin Abrasion Test >100. 000 ciclos cycles Resistencia U. V. U. V. Resistance 1. 000 horas hours Solidez a la luz Fastness to light UNE EN ISO 105 B02: 2014 (Minimum BWS**5) 6 Resistencia a la traccin Tensile Strength UNE EN ISO 3377 1:

Urdimbre - Warp: 0

Urdimbre - Warp: 0-70 % Resistencia al pilling / Pilling Strength                             ASTM D-3512 5 (sin pilling / without pilling) Acabado antimanchas                                    Resina fluorada Stain Resistant                               Flourochemical Treatment Yes Tratamiento Odox / Odox Treatment    Koo Corporation Opcional-Optional Tratamiento ignífugo / Fire Retardant Treatment Optional:

Resistencia al pilling / Pilling Strength ASTM D3512 5 (sin pilling - without pilling) Acabado antimanchas / Stain Resistant Resina fluorada / Fluorochemical treatment Tratamiento Odox / Odox Treatment KAO CORPORATION Opcional / Optional Tratamiento ignífugo / Fire Retardant Treatment OPTIONAL: UNE 1021 Parts 1 and 2 BS 5852 Parts 1 (Cigarette & Match) NF P92-503 M2 IMO MSC (88) Part 8 (MED) BS 5852 CRIB 5 UNI 9175 CLASSE 1IM

CAL TB 117-2013 Selection E

Trama - Weft: 64% Urdimbre - Warp: 61%

Trama - Weft: 115 daN

Soporte - Backing: 33% Cotton - 67% Polyester

Trama - Weft: 200 N

Característica Descripción Composición – Composition Composite Synthetic Fibers Peso – Weight 500 g/m² Ancho – Width 180 cm Factor de apertura – Openness factor 22 % Resistencia a la abrasión – Abrasion Resistance 120

15 LB Solidez a la luz / Fastness to light AATCC 16

Urdimbre - Warp: 10 daN

Trama - Weft: 28 N